Polymer cement (JS) waterproof coating (also known as polymer waterproof slurry, polymer waterproof glue) is an acrylic polymer cement-based waterproof material of high performance. It is composed of acid and alkali, anti-aging, high elasticity of the acrylic polymer emulsion formed oligomers add other additives. By adding a certain percentage of cement can be formulated for different parts of the waterproof coating. Good quality and low price factory direct supply waterproof coating JS waterproof coating high polymer 1. Cost: strong bond, good weather resistance, high temperature resistant, cement-based waterproof layer formed by mixing cement, water and long life. 2. Strong adhesion to the substrate: according to a certain proportion of cement mixing, may be applied to the wet surface of the base, after hard work and the substrate to form a watertight whole, without hollowing, shedding phenomenon of channeling water. 3. Construction is simple: the addition of a special polymer slurry modified active substance can be mixed directly with concrete or cement mortar construction, and excellent compatibility. Good quality and low price factory direct supply waterproof coating JS waterproof polymer coating 4. Environmental: The product is non-toxic, harmless, non-polluting, state-level focus on the introduction of environmentally friendly products. 1. Ⅰ polymer cement-based waterproof coating: mainly used to make the roof waterproof layer or high performance occasions extended waterproofing. 2. Ⅱ / Ⅲ polymer cement-based waterproof coating: mainly used for basements, underground tunnels, bathroom floor, sink, etc., especially under moist and construction of long-term immersion in water conditions. 3. The polymer cement mortar Usage: mainly used for making facade tiles need to paste the parts of the waterproofing. Fourth, technical indicators of good quality and low price factory direct supply waterproof coating JS waterproof polymer coating execute GB / T 23445-2009 "polymer cement waterproof paint" standard indicators. No. Test Item Standard I II III 01 solid content,% ≥70 02 Tensile strength, Mpa ≥1.2 ≥1.8 ≥1.8 03 Elongation,% ≥200 ≥80 ≥30 04 bond strength, Mpa ≥0.50 ≥0.70 ≥ 1.00 05 impermeability (0.3MPa, 30min) impervious Fifth, use (a) coating usage 1. The base surface treatment of good quality and low price factory direct supply waterproof coating JS waterproof polymer coating the substrate surface clean, leveling, keeping no cracks, no loose; yin and yang angle arc angle made; the sharp polished place. 2. The polymer cement-based waterproof coating formulation Ⅰ polymer cement-based waterproof coating ratio (weight ratio): liquid material: 32.5R than ordinary Portland cement = 1: 0.5. Type Ⅱ polymer cement-based waterproof coating ratio (weight ratio): liquid material: 32.5R over ordinary Portland cement = 1: 1. Ⅲ polymer cement-based waterproof coating ratio (weight ratio): liquid material: 32.5R than ordinary Portland cement = 1: 2. 3. parts processing node splash wet base surface, the yin and yang corner, wall pipe, floor drain port, construction joints, etc. with type Ⅱ polymer cement-based waterproof coating and fiberglass cloth to strengthen the process, a thickness of about 1.0mm. The waterproof layer brushing predetermined proportion reclaimers, thoroughly stirred with a stirrer for about 5 minutes, until the coating material does not contain aggregate, for water, the first compound in liquid water, stirring with a stirrer slowly add the powder. Increase the amount of color pigment layer coating liquid material is 10% or less, and only need to add the pigment in the surface layer of paint. Even when applied to try to not have local deposition and require multiple brush several times so as not to leave air bubbles between the paint and the grass roots, tightly bonded. When adding non-woven construction, coating and the coating to be under continuous construction, nonwovens straight to paving, and not leave with a brush real hollowing. The first layer of non-stick directly to brush a second layer (each about 0.6mm, not too thick) after hand; general water need to brush two or more, the last time when the waterproof layer is dry dilute sprinkle sand on top, can increase their and the protective layer adhesion. After brushing the edge of the coating brush a few times to close the head; waterproof layer is completely dry. Good quality and low price factory direct supply waterproof coating JS waterproof polymer coating waterproof protective layer waterproof layer 5. After the dryness may be 1.5 to 2.0cm thick protective layer of cement mortar in accordance with demand. 6. Reference amount: Ⅰ polymer cement-based waterproof coating thickness of 1.0mm, about 0.8 ~ 1.0kg / m2. Type Ⅱ polymer cement-based waterproof coating thickness of 1.0mm, about 0.6 ~ 0.8kg / m2. Ⅲ polymer cement-based waterproof coating thickness of 1.0mm, about 0.4 ~ 0.6kg / m2. (B) mortar Usage 1) mortar waterproof layer practice: ① Primary treatment: The base surface should be smooth, firm, no cellular, Ma surface, dirt, grease and other surface deposits. ② back treatment: a polymer substrate surface to brush again, back cover treatment. ③ batch file Mortar preparation: good quality and low price factory direct supply waterproof coating JS waterproof polymer coating A Batch file: latex waterproof mortar: cement: sand = 1: 2: 4 weight ratio of uniform mixing, batch files (for surface layer or an adhesive layer). B Batch file: Mortar Water Repellent Emulsion: cement: sand = 1: 2: (4-6) in a weight ratio Stir batch file (for the bottom layer). Polymer dosage: Thickness 1cm, the amount of 1 ~ 1.5Kg / m2. 2) Waterproof and paste an integrated approach: good quality and low price factory direct supply waterproof coating JS waterproof polymer coating ① Primary treatment: The base surface should be smooth and clean, no dust sewage treatment. ② decorative material surface should be clean, too dry should be soaked in water, dried. ③ with mortar waterproof emulsion first substrate surface materials and decorative surfacing each first brush again, back cover treatment. ④ mortar waterproof emulsion: cement: sand = 1: 2: (4-6) in a weight ratio Stir and paste evenly on surface decoration materials, paste thickness of 5.0 ~ 8.0mm is then bonded in towel on the substrate, and leveling, compaction. ⑤ nature conservation at room temperature for 24 to 48 hours, five days to achieve optimal bond strength. VI Notes good quality and low price factory direct supply waterproof coating JS coating polymer waterproofing paint 1. Stir one-time run, should not be re-used rubber dryness. 2. Suitable construction temperature 5 to 45 degrees Celsius, air circulation during the construction. 3. After two days of construction, attention to anti-rain, strong sun or frost; tools and equipment after use please clean water. Seven, packaging and storage of 50 kg / barrel, 25 kg / barrel, 20 kg / barrel, 9 kg / barrel; cool place, the shelf life of six months.